Building profiles

low to very low moisture content

enables high loading of filler and plasticizer

excellent extrusion properties

high surface quality

high tensile modulus

low compression set

Solid / Light-colored

Building profile, white (similar to RAL 9002), start formulation RAL GZ 716/1 B/II and DIN 7863, very good extrudability, excellent compression set; 65 Shore A; EPDM; peroxide cure (M 612.10/4) (M 612.10/2) (M 612.10/9) (M 612.10/7)
Building profile, gray, start formulation RAL GZ 716/1 B/II, moderate gray scale change after artificial weathering; 65 Shore A; EPDM; peroxide cure (M 586.3 A) (M 586.3/28) (M 586.3/19) (M 586.3 C) (M 586.3 B)
Building profile; 55 Shore A; EPDM; sulfur cure / LCM or hot air cure (A.1.3.002)
Building profile; 75 Shore A; EPDM; sulfur cure / LCM cure (871 E 237)
Building profile; 70 Shore A; EPDM; peroxide cure / LCM cure (M 124)
Building profile; 60 Shore A; EPDM; peroxide cure / LCM cure (RRS 1)
Building profile; 20 Shore A; EPDM; sulfur cure / LCM cure (A.1.3.001)

Solid / Black

Building profile, DIN 7863; 60 Shore A; EPDM; sulfur cure / steam cure (V 5842 B)
Building profile, AFNOR 85301; 80 Shore A; EPDM; sulfur cure / CV cure (891 E 302)
Building profile, DIN 7863; 70 Shore A; EPDM; sulfur cure / steam cure (V 5843 B)
Building profile, DIN 7863; 80 Shore A; EPDM; peroxide cure / LCM cure (911 C 157)
Building profile, start formulation DIN 7863 and RAL GZ 716/1 A/II, replacement of carbon black by Aktisil VM 56; 65 Shore A; EPDM; peroxide cure (M 598.1/2) (M 598.1/14) (M 598.1/11)
Building profile, flame retardant halogen free; 80 Shore A; EPDM; sulfur cure / steam cure (911 E 514)
Building profile, AFNOR 85301; 60 Shore A; EPDM; sulfur cure / CV cure (891 E 300)
Building profile, flame retardant halogen free; 60 Shore A; EPDM; peroxide cure / steam cure (921 Y 001)
Building profile, DIN 7863; 50 Shore A; EPDM; sulfur cure / steam cure (V 5841 B)
Building profile, AFNOR 85301; 70 Shore A; EPDM; sulfur cure / CV cure (891 E 301)

Sponge / Light-colored

Density 0.40 g/cm³; EPDM; sulfur cure / LCM cure (RRS 5)
Density 0.30 g/cm³; EPDM; sulfur cure / LCM cure (A.2.4.002)
Density 0.60 g/cm³; EPDM; sulfur cure / hot air cure (RRS 7)
Density 0.35 g/cm³; EPDM; sulfur cure / LCM cure (A.2.4.003)
Density 0.45 g/cm³; EPDM; peroxide cure / LCM cure (RRS 6)
Density 0.35 g/cm³; EPDM; sulfur cure / LCM cure (RRS 2)
Density 0.40 g/cm³; EPDM; sulfur cure / LCM cure (RRS 3)
Density 0.40 g/cm³; EPDM; sulfur cure / LCM cure (RRS 4)
Density 0.50 g/cm³; EPDM; sulfur cure / LCM cure (A.2.4.001)

Sponge / Black

Density 0.35 g/cm³; EPDM; peroxide cure / LCM cure (871 M 135)
Density 0.40 g/cm³; EPDM; sulfur cure / LCM cure (921 M 051)
DIN 4060 (1988-12); Density 0.80 g/cm³; EPDM; sulfur cure / UHF cure (V 2155)

Download all

Technical Report

technical-report

Technical Poster

technische-poster

Recommended Products

Name	Short Description
SILLITIN Z 86	Standard product for black profiles.
SILLIKOLLOID P 87	Same as Sillitin Z 86, but with best extrusion quality/edge smoothness and collapse resistance of complex profiles even at high extrusion speed.
AKTISIL VM 56	Same as Sillitin Z 86, but with higher tensile strength, higher tensile modulus and lower compression set, higher loading of filler/ plasticizer.
SILLITIN Z 89	Similar to Sillitin Z 86, standard product for color profiles,
AKTISIL VM 56/89	Same as Sillitin Z 89, but with higher tensile strength, higher tensile modulus and lower compression set, higher loading of filler/plasticizer.
SILFIT Z 91	Avoidance of deposits on dies caused by filler, greater brightness and color neutrality, less moisture content, improved dispersion, lower compression set, very fine cell structure in sponge rubber profiles.
AKTIFIT VM	Same as Silfit Z 91, but with very low moisture content, higher tensile strength, higher tensile modulus, lower compression set, higher loading of filler/plasticizer.