soft, chemically foamed
Sillikolloid P 87 offers best extrusion quality/edge smoothness of complex profiles even at high extrusion speed and slightly higher tensile strength.
- good mixing and dispersion properties
- good extrusions properties
- high surface quality
- high electrical resistance
- cost reduction potential
- avoid deposits on dies caused by filler
- lower water absorption (compared with carbon black)
| Product characteristics | Unit | Testing method | SILLIKOLLOID P 87 |
|---|---|---|---|
|
Color values L*
Color values a*
Color values b*
|
acc. to CIELAB |
94.5
0.9
9.0
|
|
|
Particle size D50
Particle size D97
|
µm | acc. to ISO 13320-1 |
1.5
6.5
|
|
Residue > 40 µm
|
mg/kg | acc. to DIN EN ISO 787 part 18 |
20
|
| Volatile matter at 105 °C | % | acc. to DIN EN ISO 787 part 2 | 0.5 |
| pH Value | acc. to DIN EN ISO 787 part 9 | 8.7 | |
|
Density
Bulk density
Tamped density
|
g/cm³ |
acc. to DIN EN ISO 787 part 10
acc. to DIN ISO 903-1976
acc. to DIN EN ISO 787 part 11
|
2.6
0.25
0.40
|
|
Spec. Surface area (BET)
Oil absorption
|
m²/g
g/100 g
|
acc. to DIN ISO 9277
acc. to DIN EN ISO 787 part 5
|
14
55
|
|
Hardness silica/kaolinite
Abrasivity
|
mg |
acc. to Mohs
acc. to Einlehner
|
7/2.5
25
|
| Refractive index n | sin α / sin β | 1.55 | |
|
Water solubility
Acid solubility
|
% |
acc. to DIN EN ISO 787 part 3
acc. to DIN 53770 (0,1 N HCL)
|
< 0.5
< 1
|
|
Chemical Analysis:
SiO2
Al2O3
Fe2O3
|
% | acc. to DIN 51001 (RFA) |
80
14
< 1
|
|
Mineralogical Composition:
Neuburg silica
Kaolinite
Other minerals
|
% | Based on X-ray diffraction pattern analysis combined with Rietveld |
55
30
5
|
soft, chemically foamed
In order to make available to you the most important information about our products at all times, you will find here the Material Specification.
The aspects to observe when working with our products are detailed in our Material Safety Data Sheet, which also can be downloaded.
All information about material characteristics, application fields and benefits can be found in this Technical Data Sheet and is also for download available here.