- good extrusion properties and collapse resistance
- reduced stickiness
- no blooming
- drier surface
- very good oil resistance
- low tension and compression set without post cure
- partial replacement of ATH with Aktisil Q, Aktifit Q or Silfit Z 91 provides practically the same flame-retardant properties of pure ATH
peroxide
- Silicone rubber compounds with Aktisil Q, curing agent "2,5-Bis-(t-butylperoxy)-2,5-dimethylhexane"; 40-75 Shore A; Q; peroxide cure (M 608.5/22) (M 608.5/18) (M 608.5/19) (M 608.5/20) (M 608.5/21)
- Silicone rubber compounds, Elastosil R 401; Optimization of Property Combinations with Aktisil Q ; 45-50 Shore A; Q; peroxide cure (M 655.0/2) (M 655.0/5) (M 655.0/21) (M 655.0/22) (M 655.0/25) (M 655.0/1)
- Silicone rubber compounds, Elastosil R 752; Optimization of Property Combinations with Aktisil Q ; 50-60 Shore A; Q; peroxide cure (M 655.1/17) (M 655.1/2) (M 655.1/3) (M 655.1/6) (M 655.1/13) (M 655.1/14)
- Silicone rubber compounds, combination of Aktisil Q with quartz flour; 40-45 Shore A; Q; peroxide cure (M 626.2/4) (M 626.2/10) (M 626.2/24) (M 626.2/30)
- Silicone rubber compounds with Silfit Z 91, curing agent "Bis-(2,4-dichlorobenzoyl) peroxide"; 45-65 Shore A; Q; peroxide cure (M 619.1/4) (M 619.1/1) (M 619.1/2) (M 619.1/3)
- Silicone rubber compounds, Elastosil R 420; Optimization of Property Combinations with Aktisil Q ; 40-50 Shore A; Q; peroxide cure (M 655.0/12) (M 655.0/15) (M 655.0/31) (M 655.0/32) (M 655.0/35) (M 655.0/11)
- Silicone rubber compounds; Alternative chlorine-free peroxide - Benefits with Aktisil Q ; 40-70 Shore A; Q; peroxide (M 670.0/11) (M 670.0/1) (M 670.0/12) (M 670.0/2) (M 670.0/13) (M 670.0/3) (M 670.0/14) (M 670.0/4) (M 670.0/15) (M 670.0/5)
- Silicone rubber compounds, flame retardant; 60-70 Shore A; Q; peroxide cure (M 617.0/12) (M 617.0/7) (M 617.0/11)
- Silicone rubber compounds with Aktisil Q, curing agent "Bis-(2,4-dichlorobenzoyl) peroxide"; 40-75 Shore A; Q; peroxide cure (M 608.5/1) (M 608.5/8) (M 608.5/9) (M 608.5/10) (M 608.5/11)
- Silicone rubber compounds with Aktisil Q, curing agent "Dicumyl peroxide"; 40-75 Shore A; Q; peroxide cure (M 608.5/29) (M 608.5/30) (M 608.5/31) (M 608.5/32) (M 608.5/33)
addition cured
- Silicone rubber compounds; Neuburg Siliceous Earth in addition-cured high consistency silicone rubber, molding, high tear resistance; 40-50 Shore A; Q; addition-cured (M 675.0/41) (M 675.0/42) (M 675.0/44) (M 675.0/45) (M 675.0/43)
Technical Report
- Silfit Z 91 in silicone rubber
- Neuburg Siliceous Earth in high consistency silicone rubber
- Neuburg Siliceous Earth in combination with ATH - Flame retardancy of silicone rubber
- Alternative chlorine-free peroxide - Benefits with Aktisil Q
- Peroxide cured silicone rubber - Optimization of property combinations with Aktisil Q
- Neuburg Siliceous Earth in addition cured high consistency silicone rubber
Technical Poster
- Aktisil Q in combination with quartz flour (technical poster)
- Aktisil Q in high consistency silicone rubber (technical poster)
- Alternative chlorine-free peroxide - Benefits with Aktisil Q (technical poster)
- Neuburg Siliceous Earth in combination with ATH - Flame retardancy of silicone rubber (technical poster)
- Peroxide cured silicone rubber - Optimization of property combinations with Aktisil Q (technical poster)
- Neuburg Siliceous Earth in addition cured high consistency silicone rubber (technical poster)