STP-E / STP-U
Calcined product, alkyl functionalized.
Aktifit PF 111 offers high rheological activity (higher viscosity at low shear rates, yield point, greater shear thinning) with high tensile and lap shear strength. as well as highest tear resistant in STP-U.
- selectable rheology (free-flowing to non-sagging)
- excellent strength of properties, up to 2-fold or 3-fold calcium carbonate (tensile strength and lap shear strength), mostly without reducing the ultimate elongation
- good water resistance and chemical resistance
| Product characteristics | Unit | Testing method | AKTIFIT PF 111 |
|---|---|---|---|
| Functionalization | alkyl | ||
|
Color values L*
Color values a*
Color values b*
|
acc. to CIELAB |
96.2
- 0.1
1.0
|
|
|
Particle size D50
Particle size D97
|
µm | acc. to ISO 13320-1 |
2.3
11.0
|
|
Residue > 40 µm
|
mg/kg | acc. to DIN EN ISO 787 part 18 |
10
|
| Volatile matter at 105 °C | % | acc. to DIN EN ISO 787 part 2 | 0.2 |
| Electrical conductivity | µS/cm | acc. to DIN EN ISO 787 part 14 | not applicable |
|
Density
Bulk density
Tamped density
|
g/cm³ |
acc. to DIN EN ISO 787 part 10
acc. to DIN ISO 903-1976
acc. to DIN EN ISO 787 part 11
|
2.6
0.35
0.65
|
|
Spec. Surface area (BET)
Oil absorption
|
m²/g
g/100 g
|
acc. to DIN ISO 9277
acc. to DIN EN ISO 787 part 5
|
9
55
|
|
Hardness silica/kaolinite
|
mg |
acc. to Mohs
|
7/4.5
|
| Refractive index n | sin α / sin β | 1.55 | |
|
Water solubility
Acid solubility
|
% |
acc. to DIN EN ISO 787 part 3
acc. to DIN 53770 (0,1 N HCL)
|
not applicable
not applicable
|
|
Chemical Analysis:
SiO2
Al2O3
Fe2O3
|
% | acc. to DIN 51001 (RFA) |
86
13
< 1
|
|
Mineralogical Composition:
Neuburg silica
Calcined kaolinite
|
% | Based on X-ray diffraction pattern analysis combined with Rietveld |
60
40
|
|
Equilibrium moisture content at 25°C
and 50% relative humidity
and 80% relative humidity
and 90% relative humidity
|
% | acc. to DIN 66138 |
0.07
0.10
0.13
|
| Water absorption | ml/g | acc. to Baumann | ≤ 0.1 |
| hydrophobic | X |