Sillikolloid P 87 puriss creates because of its finest particle smooth polishing properties and because of its low residue no scratch marks. The product also offers less residue and improved dispersion.
- excellent dispersion properties
- very low sedimentation
- good cut
- gentle cleaning
- no scratching
- acid-resistant
- also suitable for food contact and drinking water applications (as per FDA and BfR regulations)
- suitable for glass, ceramic, metal, natural stone, pedestal, plastic, porcelain, stainless steel
Product characteristics | Unit | Testing method | SILLIKOLLOID P 87 puriss |
---|---|---|---|
Color values L*
Color values a*
Color values b*
|
acc. to CIELAB |
94.5
0.9
9.0
|
|
Particle size D50
Particle size D97
|
µm | acc. to ISO 13320-1 |
1.5
6.0
|
Residue > 40 µm
|
mg/kg | acc. to DIN EN ISO 787 part 18 |
8
|
Volatile matter at 105 °C | % | acc. to DIN EN ISO 787 part 2 | 0.5 |
Electrical conductivity | µS/cm | acc. to DIN EN ISO 787 part 14 | 80 |
pH Value | acc. to DIN EN ISO 787 part 9 | 8.7 | |
Dispersion time in ester plasticizer | min | UGR-PV/PT/67 | 8 |
Density
Bulk density
Tamped density
|
g/cm³ |
acc. to DIN EN ISO 787 part 10
acc. to DIN ISO 903-1976
acc. to DIN EN ISO 787 part 11
|
2.6
0.20
0.34
|
Oil absorption
|
g/100 g
|
acc. to DIN EN ISO 787 part 5
|
55
|
Hardness silica/kaolinite
Abrasivity
|
mg |
acc. to Mohs
acc. to Einlehner
|
7/2.5
20
|
Refractive index n | sin α / sin β | 1.55 | |
Water solubility
Acid solubility
|
% |
acc. to DIN EN ISO 787 part 3
acc. to DIN 53770 (0,1 N HCL)
|
< 0.5
< 1
|
Chemical Analysis:
SiO2
Al2O3
Fe2O3
|
% | acc. to DIN 51001 (RFA) |
80
14
< 1
|
Mineralogical Composition:
Neuburg silica
Kaolinite
Other minerals
|
% | Based on X-ray diffraction pattern analysis combined with Rietveld |
55
30
5
|
- Stove cleaner (RR 017)
- Brass and bronze polish 553-LR (RR 015)
- Silicone and wax remover (RR 021)