- very low sieve residue
- very low chloride content
- long flow time with short vulcanization time
- high tensile modulus
- low compression set
- good hot air aging properties
- sealing tightness at high soldering temperatures
resin cure
- Medium mineral filler / carbon black loading; 70/75 Shore A; IIR; resin cure (M 620.1/4) (M 620.1/3) (M 620.1/8)
- High mineral filler / low carbon black loading, with phenolic crosslinker resin; 80/85 Shore A; IIR; resin cure (M 620.0/20) (M 620.0/17) (M 620.0/13) (M 620.0/12)
- High mineral filler / low carbon black loading; 75/80 Shore A; IIR; resin cure (M 620.0/19) (M 620.0/8) (M 620.0/4) (M 620.0/3)
Sulfur cure
- 70 Shore A; IIR; sulfur cure (M 231.0/1)
Recommended Products
Sorted by crosslinking agent.