Sillikolloid P 87 offers best extrusion quality/edge smoothness and collapse resistance of complex profiles and stability as well as lesser matting effect,
higher tensile strength, tear resistance and least wear.
- good extrusion properties
- high surface quality
- low moisture content
- high tensile modulus
- low compression set
- high electrical resistance (compared with carbon black)
| Product characteristics | Unit | Testing method | SILLIKOLLOID P 87 |
|---|---|---|---|
|
Color values L*
Color values a*
Color values b*
|
acc. to CIELAB |
94.5
0.9
9.0
|
|
|
Particle size D50
Particle size D97
|
µm | acc. to ISO 13320-1 |
1.5
6.5
|
|
Residue > 40 µm
|
mg/kg | acc. to DIN EN ISO 787 part 18 |
20
|
| Volatile matter at 105 °C | % | acc. to DIN EN ISO 787 part 2 | 0.5 |
| pH Value | acc. to DIN EN ISO 787 part 9 | 8.7 | |
|
Density
Bulk density
Tamped density
|
g/cm³ |
acc. to DIN EN ISO 787 part 10
acc. to DIN ISO 903-1976
acc. to DIN EN ISO 787 part 11
|
2.6
0.25
0.40
|
|
Spec. Surface area (BET)
Oil absorption
|
m²/g
g/100 g
|
acc. to DIN ISO 9277
acc. to DIN EN ISO 787 part 5
|
14
55
|
|
Hardness silica/kaolinite
Abrasivity
|
mg |
acc. to Mohs
acc. to Einlehner
|
7/2.5
25
|
| Refractive index n | sin α / sin β | 1.55 | |
|
Water solubility
Acid solubility
|
% |
acc. to DIN EN ISO 787 part 3
acc. to DIN 53770 (0,1 N HCL)
|
< 0.5
< 1
|
|
Chemical Analysis:
SiO2
Al2O3
Fe2O3
|
% | acc. to DIN 51001 (RFA) |
80
14
< 1
|
|
Mineralogical Composition:
Neuburg silica
Kaolinite
Other minerals
|
% | Based on X-ray diffraction pattern analysis combined with Rietveld |
55
30
5
|
Solid / Black
In order to make available to you the most important information about our products at all times, you will find here the Material Specification.
The aspects to observe when working with our products are detailed in our Material Safety Data Sheet, which also can be downloaded.
All information about material characteristics, application fields and benefits can be found in this Technical Data Sheet and is also for download available here.